ThermoWhite® WD 130 R
Mineral bonded thermal insulation for high loads.
Our insulation fill made of pure recycled granules with good values in thermal and impact sound insulation.
- Use of pure recycled granules
- Good thermal insulation
- Lambda = 0,055 W/mK
- Traffic loads up to 20 kN/m²
- Enormous compressive strength
- Compressive stress CS (10) 70 = 80 kPa
Technical data: ThermoWhite WD 130 R
Designation code: BEPS-WD 130 R-PS(0-8)R-LD120-FMD160_DMD145-MU6-CS(10/70-CC(1,2/0,5/10)10-DLT(1)5
| 90%-Fractile value of thermal conductivity (dry) - λ10 dry, 90/90 | 0,0550 W/mK |
| Design value of thermal conductivity - λ | 0,057 W/mK |
| Bulk density of EPS dry mortar - LD | 120 kg/m³ |
| Density of fresh mortar - FMD | 160 kg/m³ |
| Dry bulk density - DMD | 145 kg/m³ |
| Compressive stress at 10 % deformation - CS (10)100 | 100 kPa |
| Dimensional stability under compressive and temperature stresses - DLT (1)5 | ≤ 3 % |
| Water vapour permeability - at 3 cm | µ*d = ≤ 6 m |
| Water absorption during brief, partial immersion | ≤ 2,0 kg/m² |
| Reaction to fire according to EUROCLASS*** | B-S1 |
| Type and particle size group of EPS aggregate | 0 - 8 R |
| Addition of water each m³ | 45 litre |
| Minimum thickness**** | 25 mm |
| Compressibility under charge (Diff. between dL and dF) - with 5 kPa (500 kg/m²) | 0,3 mm |
| Processing time (open time, 20°/60 % LF) | min. 40 Minutes |
| Processing temperature min/max | +5° / +35°C |
| walkable from | 24 hours* |
| Ready for covering after (CM-measurement) | ≤ 15 CM-% |
| On installed thickness to 200 mm (23 °C / 50 % LF) | approx. 2 days** |
| Compensation moisture on ÖNORM EN 12429 | 5,5 M % |
| Impact sound reduction (according to EN ISO 717-2) | 25 dB |
| Dynamic Stiffness | 134 MN/m³ |
| Live loads - 10 cm | 19 kN/m² |
* depending on temperature and humidity.
** the data are to be understood as guide values. A CM measurement is required.
*** A thermal insulation material made of EPS can prevent the spread of fire in case of fire, however, it does not constitute a fire barrier.
** the data are to be understood as guide values. A CM measurement is required.
*** A thermal insulation material made of EPS can prevent the spread of fire in case of fire, however, it does not constitute a fire barrier.
ThermoWhite® Ready-mixed products
The ThermoWhite® ready-mixed product is the dry mixture of Thermowhite compound and EPS granules.
Ideal for craftsmen and small quantities, it can be mixed and installed directly on the construction site by adding water in a compulsory mixer.
ThermoWhite® ready-mixed product is mainly used for small quantities, for example for renovations and extensions. Available in bags of 100 and 200 liters.